ASME 焊工角焊缝破坏试验

    角焊缝断裂试验是一种通过破坏焊缝的方式来检验根部焊缝熔覆情况的机械试验方法，可以很好的检查整个角焊缝根部的焊透与否的情况。而借助宏观腐蚀试验可以更清晰的看到根部焊缝的熔覆深度。

      在ASME 焊工考试时，通常我们不进行角焊缝焊工考试，因为其覆盖范围较小。在ASME IX中QW-303.2条款有明确规定，原文摘自如下:

QW-303.2 Fillet Welds — General.  Welders and welding operators who pass the required tests for fillet welds in the test positions of Table QW-461.9 shall be qualified for the positions of fillet welds, and tack welds in joints to be fillet welded, shown in Table QW-461.9. Welders and welding operators who pass the tests for fillet welds shall be qualified to make tack welds in joints to be fillet welded as limited in Table QW-461.9 and fillet welds only in the thicknesses of material, sizes of fillet welds, and diameters of pipe and tube 2-7/8 in. (73 mm) O.D. and over, as shown in Table QW-452.5, within the applicable essential variables. Welders and welding operators who make fillet welds on pipe or tube less than 2-7/8 in. (73 mm) O.D. must pass the pipe fillet weld test per Table QW-452.4 or the required mechanical tests in QW-304 and QW-305 as applicable.

     文中提到了角焊缝焊工技能考试的位置、材料规格所能覆盖的方位。要特别注意。

       做断裂试验时，整个板将会被压平，根部不允许出现裂纹及未焊透情况。断裂试样夹渣、表面可见气孔的总长度不允许超过 3/8 in (10 mm) 。具体的试样焊接准备如下图所示：

角焊缝破坏试验注意事项： 

1、材料尺寸的选择，板材长度≥150mm。

2、只在单侧焊接角焊缝，曾经碰到过有的单位焊接工程师错误的指导工人焊接双面角焊缝，完全错误。

3、角焊缝焊接过程中，必须大概在焊缝总长的中间位置处熄弧停留，然后再次焊接，中间位置停留主要是为了考察焊工接头的技能。

4、焊接试件完成后，去除左右两侧各25mm长的试样，已做宏观检测，查看焊缝是否熔合良好。

5、注意图中给出的提示，注意断裂试验所施加力的方向。见下图示：

更多动态，请关注我们官方网站：www.tuxren.com，或者关注我们的微信平台：asmecn

     本文系网络转载，如涉及作品版权问题，请与我们联系

ASME中国制造感谢您一直以来的支持, 谢谢！